| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 124 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6890 | MPa | ASTM D790 |
| Hardness, Rockwell R | 109 | - | ASTM D785 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 101 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 215 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 198 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ASTM E831 |
| CTE, 60°C to 138°C, flow | 2.52E-05 | 1/°C | ASTM E831 |
| PHYSICAL |
|---|
| Specific Gravity | 1.51 | - | ASTM D792 |
| Specific Volume | 0.66 | cm³/g | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.3-0.4 | % | SABIC method |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.4-0.6 | % | SABIC method |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.6-0.8 | % | SABIC method |
| ELECTRICAL |
|---|
| Volume Resistivity | 1.E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength, in oil, 3.2 mm | 17.9 | kV/mm | ASTM D149 |
| Relative Permittivity, 50/60 Hz | 3.53 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 3.32 | - | ASTM D150 |
| Dissipation Factor, 50/60 Hz | 0.008 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.013 | - | ASTM D150 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E121562-477264 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255-275 | °C | |
| Nozzle Temperature | 255-270 | °C | |
| Front - Zone 3 Temperature | 255-265 | °C | |
| Middle - Zone 2 Temperature | 250-260 | °C | |
| Rear - Zone 1 Temperature | 245-255 | °C | |
| Mold Temperature | 65-95 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |