| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 39 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.9 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 56 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1790 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 870 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 801 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 98 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 47 | °C | ASTM D648 |
| PHYSICAL |
|---|
| Specific Gravity | 1.22 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 2.4-2.7 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 2.4-2.7 | % | SABIC method |
| Melt Flow Rate, 250°C/5.0 kgf | 12.7 | g/10 min | ASTM D1238 |
| Melt Viscosity | 1200 | Pa-s | SABIC method |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 240 - 255 | °C | |
| Front - Zone 3 Temperature | 245 - 260 | °C | |
| Middle - Zone 2 Temperature | 240 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 250 | °C | |
| Mold Temperature | 50 - 75 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Shot to Cylinder Size | 40 - 80 | % | |
| Vent Depth | 0.013 - 0.025 | mm | |