| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 15 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D638 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 10 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2550 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 145 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 117 | - | ISO 2039-2 |
| IMPACT |
|---|
| Charpy Impact, unnotched, 23°C | NB | kJ/m² | ISO 179/2C |
| Charpy Impact, unnotched, -30°C | 80 | kJ/m² | ISO 179/2C |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 38 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 36 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 36 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 100 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 4 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 4 | kJ/m² | ISO 179/2C |
| THERMAL |
|---|
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D1525 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 185 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 150 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 50 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Specific Gravity | 1.31 | - | ASTM D792 |
| Mold Shrinkage on Tensile Bar, flow | 1.3-2.0 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 1.1-2.0 | % | SABIC method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.34 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 20 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 50 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 165 | Pa-s | ISO 11443 |
| Injection Molding |
|---|
| Drying Temperature | 110-120 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-270 | °C | |
| Nozzle Temperature | 240-260 | °C | |
| Front - Zone 3 Temperature | 245-265 | °C | |
| Middle - Zone 2 Temperature | 240-255 | °C | |
| Rear - Zone 1 Temperature | 230-245 | °C | |
| Hopper Temperature | 40-60 | °C | |
| Mold Temperature | 40-100 | °C | |