| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 10000 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7900 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 125 | - | ISO 2039-2 |
| IMPACT |
|---|
| Charpy Impact, unnotched, 23°C | 65 | kJ/m² | ISO 179/2C |
| Charpy Impact, unnotched, -30°C | 60 | kJ/m² | ISO 179/2C |
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 880 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 100 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 100 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 55 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 11 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, -30°C | 12 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, flow | 1.98E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 1.73E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 140 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.54 | - | ASTM D792 |
| Filler Content | 30 | % | ASTM D229 |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D1238 |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.26 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 150 | Pa-s | ISO 11443 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D149 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D149 |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D149 |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0016 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-236594 | - | - |
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Injection Molding |
|---|
| Drying Temperature | 110-120 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-270 | °C | |
| Nozzle Temperature | 240-260 | °C | |
| Front - Zone 3 Temperature | 245-265 | °C | |
| Middle - Zone 2 Temperature | 240-255 | °C | |
| Rear - Zone 1 Temperature | 230-245 | °C | |
| Hopper Temperature | 40-60 | °C | |
| Mold Temperature | 40-100 | °C | |