| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Taber Abrasion, CS-17, 1 kg | 50 | mg/1000cy | SABIC method |
| Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 170 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8000 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 122 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 119 | - | ISO 2039-2 |
| IMPACT |
|---|
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 1.05E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 217 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 175 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 206 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 160 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.4-0.6 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method |
| Density | 1.5 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.09 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Dielectric Strength, shorttime, 1.0mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.0014 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.013 | - | IEC 60250 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Comparative Tracking Index, M | 150 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-236608 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 21 | % | ISO 4589 |
| Injection Molding |
|---|
| Drying Temperature | 110-120 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-270 | °C | |
| Nozzle Temperature | 240-260 | °C | |
| Front - Zone 3 Temperature | 245-265 | °C | |
| Middle - Zone 2 Temperature | 240-255 | °C | |
| Rear - Zone 1 Temperature | 230-245 | °C | |
| Hopper Temperature | 40-60 | °C | |
| Mold Temperature | 40-100 | °C | |