| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 57 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 103 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4130 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 389 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 187 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 105 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 5.58E-05 | 1/°C | ASTM E831 |
| PHYSICAL |
|---|
| Specific Gravity | 1.49 | - | ASTM D792 |
| Mold Shrinkage, flow, 1.5-3.2 mm | 1.4-1.6 | % | SABIC method |
| Mold Shrinkage, flow, 3.2-4.6 mm | 1.5-1.6 | % | SABIC method |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 1.3-1.4 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 1.4-1.5 | % | SABIC method |
| ELECTRICAL |
|---|
| Dielectric Strength, in oil, 3.2 mm | 16.9 | kV/mm | ASTM D149 |
| Relative Permittivity, 50/60 Hz | 3.1 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 2.9 | - | ASTM D150 |
| Dissipation Factor, 50/60 Hz | 0.0039 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D150 |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-265 | °C | |
| Nozzle Temperature | 245-260 | °C | |
| Front - Zone 3 Temperature | 250-265 | °C | |
| Middle - Zone 2 Temperature | 245-260 | °C | |
| Rear - Zone 1 Temperature | 240-255 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |