| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 103 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 103 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3550 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 150 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4640 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 98 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 98 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5250 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4750 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 400 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 218 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 193 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 |
| PHYSICAL |
|---|
| Specific Gravity | 1.41 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7-0.9 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 1-1.2 | % | SABIC method |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 17 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-101938098 | - | - |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4520 | MPa | ASTM D790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 9.7 | % | ASTM D790 |
| Instrumented Impact, Total Energy, 23°C | 6 | J | ASTM D3763 |
| PROPERTIES AFTER 1008 HOURS AT 125°C |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 98 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4820 | MPa | ASTM D790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 7 | % | ASTM D790 |
| Instrumented Impact, Total Energy, 23°C | 5 | J | ASTM D3763 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 89 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.3 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5100 | MPa | ASTM D790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 6 | % | ASTM D790 |
| Instrumented Impact, Total Energy, 23°C | 4 | J | ASTM D3763 |
| PROPERTIES AFTER 1008 HOURS AT 155°C |
|---|
| Tensile Stress, brk, Type I, 5 mm/min | 4812 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 97.2 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 0 | MPa | ASTM D790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 3.8 | % | ASTM D790 |
| Injection Molding |
|---|
| Drying Temperature | 60-75 | °C | |
| Drying Time | 4-6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 250-265 | °C | |
| Nozzle Temperature | 245-260 | °C | |
| Front - Zone 3 Temperature | 250-265 | °C | |
| Middle - Zone 2 Temperature | 245-260 | °C | |
| Rear - Zone 1 Temperature | 240-255 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |