| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield | 96 | MPa | SABIC - Japan Method |
| Tensile Strain, break | 5-5 | % | SABIC - Japan Method |
| Flexural Stress | 128 | MPa | ASTM D790 |
| Flexural Modulus | 6080 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 137 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |
| CTE, -30°C to 30°C | 0.00003-0.00003 | 1/°C | TMA |
| PHYSICAL |
|---|
| Specific Gravity | 1.42 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.2-0.4 | % | SABIC method |
| Mold Shrinkage, flow, 6.4 mm | 0.6-0.8 | % | SABIC method |
| ELECTRICAL |
|---|
| Surface Resistivity | 1.E+16 | Ω | ASTM D257 |
| Relative Permittivity, 50/60 Hz | 3 | - | ASTM D150 |