| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 |
| IMPACT |
|---|
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 65 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Specific Gravity | 1.39 | - | ASTM D792 |
| Filler Content | 20 | % | ASTM D229 |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D1238 |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.1 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D149 |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D149 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D149 |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D150 |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Volume Resistivity | >1.E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+16 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Comparative Tracking Index, M | 100 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 23 | % | ISO 4589 |
| Injection Molding |
|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Front - Zone 3 Temperature | 245 - 265 | °C | |
| Middle - Zone 2 Temperature | 240 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 245 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 40 - 100 | °C | |