| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 165 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 68 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1720 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 801 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 534 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 48 | J | ASTM D3763 |
| Instrumented Impact Energy @ peak, -40°C | 55 | J | ASTM D3763 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 115 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 96 | °C | ASTM D648 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.17 | - | ASTM D792 |
| Specific Volume | 0.85 | cm³/g | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.13 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 1-1.2 | % | SABIC method |
| ELECTRICAL |
|---|
| Volume Resistivity | 9.5E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength, in air, 1.6 mm | 28.7 | kV/mm | ASTM D149 |
| Dielectric Strength, in air, 3.2 mm | 19.8 | kV/mm | ASTM D149 |
| Relative Permittivity, 100 Hz | 2.93 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 2.95 | - | ASTM D150 |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.03 | - | ASTM D150 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E121562-220839 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.49 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4-6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260-275 | °C | |
| Nozzle Temperature | 255-270 | °C | |
| Front - Zone 3 Temperature | 255-275 | °C | |
| Middle - Zone 2 Temperature | 250-270 | °C | |
| Rear - Zone 1 Temperature | 245-265 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 50-80 | % | |
| Vent Depth | 0.013-0.02 | mm | |