| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 32 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 145 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 1780 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 63 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1780 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 41 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 31 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.9 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 19.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1830 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 60 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1690 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 897 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 667 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 56 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 54 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 51 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 72 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 123 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 98 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 60 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.89E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 9.89E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 121 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 50 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Specific Volume | 0.83 | cm³/g | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 1.6-1.8 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 1.6-1.8 | % | SABIC method |
| Melt Flow Rate, 266°C/5.0 kgf | 21.9 | g/10 min | ASTM D1238 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.14 | % | ISO 62-1 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 17 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E207780-101089446 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.47 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 105-115 | °C | |
| Drying Time | 2-4 | Hrs | |
| Drying Time (Cumulative) | 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-270 | °C | |
| Nozzle Temperature | 250-270 | °C | |
| Front - Zone 3 Temperature | 250-265 | °C | |
| Middle - Zone 2 Temperature | 240-255 | °C | |
| Rear - Zone 1 Temperature | 230-245 | °C | |
| Mold Temperature | 40-80 | °C | |
| Back Pressure | 0.2-0.3 | MPa | |
| Shot to Cylinder Size | 50-80 | % | |
| Vent Depth | 0.013-0.02 | mm | |