| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 175 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 64 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1720 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 850 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 60 | °C | ASTM D648 |
| PHYSICAL |
|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 1.5-2 | % | SABIC method |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E207780-101488597 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Melt Temperature | 250-290 | °C | |
| Mold Temperature | 55-80 | °C | |