| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 50 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 35 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3800 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3500 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 37 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 1600 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 205 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 36 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 110 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 74 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 95 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 95 | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 111 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 101 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 118 | °C | ISO 306 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.28 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.15-0.25 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.3-0.4 | % | SABIC method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.02 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.04 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 12 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 26 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 0.4 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 290 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Front - Zone 3 Temperature | 255 - 290 | °C | |
| Middle - Zone 2 Temperature | 255 - 290 | °C | |
| Rear - Zone 1 Temperature | 250 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 60 - 90 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 30 - 80 | % | |
| Vent Depth | 0.038 - 0.076 | mm | |