| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield, 5 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3850 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3750 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 120 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| CTE, -30°C to 80°C, flow | 5.4E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 109 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 265°C/5.0 kgf | 28 | g/10 min | ASTM D1238 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.42 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 24 | cm³/10 min | ISO 1133 |
| Injection Molding |
|---|
| Drying Temperature | 110-120 | °C | |
| Drying Time | 4-6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 265-275 | °C | |
| Nozzle Temperature | 260-275 | °C | |
| Front - Zone 3 Temperature | 260-280 | °C | |
| Middle - Zone 2 Temperature | 250-275 | °C | |
| Rear - Zone 1 Temperature | 240-270 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Mold Temperature | 60-100 | °C | |