| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield, 50 mm/min | 54 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2050 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 20 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 18 | kJ/m² | ISO 180/1A |
| Charpy 0°C, V-notch Edgew 80*10*3 sp=62mm | 40 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | n.b. | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 135 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 117 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 120 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 84 | °C | ISO 75/Ae |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.7-1 | % | SABIC method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.5 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 |
| Injection Molding |
|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255 - 270 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Front - Zone 3 Temperature | 250 - 270 | °C | |
| Middle - Zone 2 Temperature | 240 - 265 | °C | |
| Rear - Zone 1 Temperature | 230 - 250 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 60 - 80 | °C | |