| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2640 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 209 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 121 | J/m | ASTM D256 |
| Izod Impact, notched, -20°C | 127 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
| Instrumented Impact Total Energy, 0°C | 67 | J | ASTM D3763 |
| Instrumented Impact Total Energy, -20°C | 72 | J | ASTM D3763 |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 103 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 90 | °C | ASTM D648 |
| PHYSICAL |
|---|
| Melt Volume Rate, MVR at 265°C/5.0 kg | 35 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E121562-101949156 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4-6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260-280 | °C | |
| Nozzle Temperature | 255-275 | °C | |
| Front - Zone 3 Temperature | 260-280 | °C | |
| Middle - Zone 2 Temperature | 255-275 | °C | |
| Rear - Zone 1 Temperature | 250-270 | °C | |
| Mold Temperature | 65-95 | °C | |
| Back Pressure | 0.3-0.6 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 50-80 | % | |
| Vent Depth | 0.013-0.02 | mm | |