| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 49 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2090 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2090 | MPa | ASTM D790 |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | ASTM D1044 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 699 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 672 | J/m | ASTM D256 |
| Izod Impact, notched, -20°C | 598 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 245 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 224 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 38 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| CTE, -30°C to 30°C, flow | 7.56E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 7.92E-05 | 1/°C | ASTM D696 |
| Thermal Conductivity | 0.18 | W/m-°C | ASTM C177 |
| Vicat Softening Temp, Rate A/50 | 140 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| PHYSICAL |
|---|
| Specific Gravity | 1.22 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.1 | % | ASTM D570 |
| Water Absorption, (23°C/Saturated) | 0.7 | % | ASTM D570 |
| Moisture Absorption, (50% RH, Equilibrium) | 0.2 | % | ASTM D570 |
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.8 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method |
| Poisson's Ratio | 0.4 | - | ASTM E132 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 4 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+14 | Ω.cm | ASTM D257 |
| Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
| Dielectric Strength, in oil, 3.2 mm | 16.9 | kV/mm | ASTM D149 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D150 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D150 |
| Injection Molding |
|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4-6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260-275 | °C | |
| Nozzle Temperature | 255-270 | °C | |
| Front - Zone 3 Temperature | 255-275 | °C | |
| Middle - Zone 2 Temperature | 250-270 | °C | |
| Rear - Zone 1 Temperature | 245-265 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 50-80 | % | |
| Vent Depth | 0.013-0.02 | mm | |