| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 155 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 125 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 82 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.7-1.1 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.8-1.1 | % | SABIC method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.5 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-236626 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 90-100 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255-270 | °C | |
| Nozzle Temperature | 250-265 | °C | |
| Front - Zone 3 Temperature | 250-270 | °C | |
| Middle - Zone 2 Temperature | 240-265 | °C | |
| Rear - Zone 1 Temperature | 230-250 | °C | |
| Hopper Temperature | 40-60 | °C | |
| Mold Temperature | 60-80 | °C | |