| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1960 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 115 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 72 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1870 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 800 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 690 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 640 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 54 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 52 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 44 | kJ/m² | ISO 180/1A |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 110 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 90 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 79 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Specific Volume | 0.83 | cm³/g | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8-1 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.8-1 | % | SABIC method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 6 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E207780-100080987 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4-6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260-275 | °C | |
| Nozzle Temperature | 255-270 | °C | |
| Front - Zone 3 Temperature | 255-275 | °C | |
| Middle - Zone 2 Temperature | 250-270 | °C | |
| Rear - Zone 1 Temperature | 245-265 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 50-80 | % | |
| Vent Depth | 0.013-0.02 | mm | |