| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 25 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2400 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 70 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 40 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 73 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D256 |
| Izod Impact, notched, 0°C | 83 | J/m | ASTM D256 |
| Izod Impact, notched, -20°C | 75 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL |
|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 46 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.7E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | NA | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 165 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 46 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.34 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 26 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-101938116 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 60-75 | °C | |
| Drying Time | 4-5 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 250-265 | °C | |
| Nozzle Temperature | 245-260 | °C | |
| Front - Zone 3 Temperature | 250-265 | °C | |
| Middle - Zone 2 Temperature | 245-260 | °C | |
| Rear - Zone 1 Temperature | 240-255 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |