| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 120 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 9300 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 189 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7580 | MPa | ASTM D790 |
| Hardness, Rockwell R | 118 | - | ASTM D785 |
| Tensile Stress, yield, 5 mm/min | 125 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 125 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 195 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 801 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 8 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 203 | °C | ASTM D648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 215 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.2E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 223 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 217 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 204 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Specific Gravity | 1.53 | - | ASTM D792 |
| Specific Volume | 0.65 | cm³/g | ASTM D792 |
| Filler Content | 30 | % | ASTM D229 |
| Water Absorption, (23°C/24hrs) | 0.06 | % | ASTM D570 |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.8 | % | SABIC method |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.3-0.5 | % | SABIC method |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.5-0.8 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5-1 | % | SABIC method |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.6-0.9 | % | SABIC method |
| Melt Flow Rate, 250°C/2.16 kgf | 17 | g/10 min | ASTM D1238 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.26 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Volume Resistivity | >3.2E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength, in air, 3.2 mm | 18.7 | kV/mm | ASTM D149 |
| Dielectric Strength, in oil, 1.6 mm | 24.8 | kV/mm | ASTM D149 |
| Relative Permittivity, 100 Hz | 3.8 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 3.7 | - | ASTM D150 |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D150 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E121562-220792 | - | - |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-265 | °C | |
| Nozzle Temperature | 245-260 | °C | |
| Front - Zone 3 Temperature | 250-265 | °C | |
| Middle - Zone 2 Temperature | 245-260 | °C | |
| Rear - Zone 1 Temperature | 240-255 | °C | |
| Mold Temperature | 65-90 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |