LEXAN™ HEALTHCARE	牌号	HPS9NEU	种类	PC
LEXAN™ HEALTHCARE	产品说明	?Polycarbonate resin with high melt strength for blow moulding applications. High impact resistance. Available in transparent colors only. For medical devices and pharmaceutical applications like blow moulded containers. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable. FDA 21CFR177.1580 food contact compliant.?

SABIC LEXAN™ HEALTHCARE PC HPS9NEU 物性表

属性	典型值	UNITS	测试手段
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	62	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	65	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	7	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>70	%	ASTM D638
Tensile Modulus, 50 mm/min	2350	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	93	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2300	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	65	MPa	ISO 527
Tensile Stress, break, 50 mm/min	70	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	7	%	ISO 527
Tensile Strain, break, 50 mm/min	>70	%	ISO 527
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	95	MPa	ISO 178
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178
Hardness, Rockwell R	120	-	ISO 2039-2
IMPACT
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	NB	J/m	ASTM D4812
Izod Impact, notched, 23°C	750	J/m	ASTM D256
Izod Impact, notched, -30°C	150	J/m	ASTM D256
Falling Dart Impact (D 3029), 23°C	170	J	ASTM D3029
Izod Impact, unnotched 80103 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C	75	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	55	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	70	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	50	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50	149	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm	144	°C	ASTM D648
HDT, 1.82 MPa, 3.2 mm	129	°C	ASTM D648
CTE, -40°C to 95°C, flow	7.E-05	1/°C	ASTM E831
Specific Heat	1.25	J/g-°C	ASTM C351
Thermal Conductivity	0.2	W/m-°C	ASTM C177
Thermal Conductivity	0.2	W/m-°C	ISO 8302
CTE, 23°C to 80°C, flow	7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	148	°C	ISO 306
Vicat Softening Temp, Rate B/120	149	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	144	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	129	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.2	-	ASTM D792
Water Absorption, (23°C/Saturated)	0.35	%	ASTM D570
Water Absorption, equilibrium, 100°C	0.58	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	0.5-0.7	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	2.5	g/10 min	ASTM D1238
Density	1.2	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.35	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	2	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg	5	cm³/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm	83	%	ASTM D1003
Haze, 2.54 mm	<0.8	%	ASTM D1003
Refractive Index	1.586	-	ISO 489
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	320-345	°C
Nozzle Temperature	315-340	°C
Front - Zone 3 Temperature	320-345	°C
Middle - Zone 2 Temperature	310-330	°C
Rear - Zone 1 Temperature	300-320	°C
Mold Temperature	80-115	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	0.025-0.076	mm