| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 68 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 130 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2370 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D790 |
| Hardness, Rockwell M | 70 | - | ASTM D785 |
| Hardness, Rockwell R | 118 | - | ASTM D785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D1044 |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 110 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 801 | J/m | ASTM D256 |
| Izod Impact, notched (natural, tints) | 801 | J/m | ASTM D256 |
| Izod Impact, notched (colors) | 801 | J/m | ASTM D256 |
| Tensile Impact Strength, Type S | 577 | kJ/m² | ASTM D1822 |
| Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D3029 |
| Instrumented Dart Impact Energy @ peak, 23°C | 63 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 35 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D648 |
| CTE, -40°C to 95°C, flow | 6.84E-05 | 1/°C | ASTM E831 |
| Specific Heat | 1.25 | J/g-°C | ASTM C351 |
| Thermal Conductivity | 0.19 | W/m-°C | ASTM C177 |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 153 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 142 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Ae |
| PHYSICAL |
|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Specific Volume | 0.84 | cm³/g | ASTM D792 |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.15 | % | ASTM D570 |
| Water Absorption, (23°C/Saturated) | 0.35 | % | ASTM D570 |
| Water Absorption, equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 10.5 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
| OPTICAL |
|---|
| Light Transmission, 2.54 mm | 88 | % | ASTM D1003 |
| Haze, 2.54 mm | 1 | % | ASTM D1003 |
| Refractive Index | 1.586 | - | ASTM D542 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength, in air, 3.2 mm | 14.9 | kV/mm | ASTM D149 |
| Relative Permittivity, 50/60 Hz | 3.17 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 2.96 | - | ASTM D150 |
| Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.01 | - | ASTM D150 |
| Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| Oxygen Index (LOI) | 25 | % | ISO 4589 |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 295-315 | °C | |
| Nozzle Temperature | 290-310 | °C | |
| Front - Zone 3 Temperature | 295-315 | °C | |
| Middle - Zone 2 Temperature | 280-305 | °C | |
| Rear - Zone 1 Temperature | 270-295 | °C | |
| Mold Temperature | 70-95 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 40-70 | rpm | |
| Shot to Cylinder Size | 40-60 | % | |
| Vent Depth | 0.025-0.076 | mm | |