| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 108 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2410 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 102 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5.7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 110 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT |
|---|
| Charpy Impact, unnotched, -30°C | 5 | kJ/m² | ISO 179/2C |
| Izod Impact, notched, 23°C | 687 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 55 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 66 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 140 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 125 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 139 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 121 | °C | ISO 75/Ae |
| PHYSICAL |
|---|
| Specific Gravity | 1.18 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 39 | g/10 min | ASTM D1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.27 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 36 | cm³/10 min | ISO 1133 |
| OPTICAL |
|---|
| Light Transmission, 2.54 mm | 88 | % | ASTM D1003 |
| Haze, 2.54 mm | <1 | % | ASTM D1003 |
| FLAME CHARACTERISTICS |
|---|
| UL Compliant, 94V-2 Flame Class Rating | 3 | mm | UL 94 by SABIC-IP |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280-300 | °C | |
| Nozzle Temperature | 270-290 | °C | |
| Front - Zone 3 Temperature | 280-300 | °C | |
| Middle - Zone 2 Temperature | 270-290 | °C | |
| Rear - Zone 1 Temperature | 260-280 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Mold Temperature | 80-100 | °C | |