| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 41 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 68 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3970 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3570 | MPa | ASTM D790 |
| Hardness, Rockwell R | 122 | - | ASTM D785 |
| Flexural Stress, yield, 2 mm/min | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3540 | MPa | ISO 178 |
| IMPACT |
|---|
| Charpy Impact, unnotched, 23°C | 1 | kJ/m² | ISO 179/2C |
| Izod Impact, notched, 23°C | 21 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 13 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 1 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 1 | kJ/m² | ISO 180/1A |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 98 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 87 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 102 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 84 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Specific Gravity | 1.08 | - | ASTM D792 |
| Melt Flow Rate, 230°C/3.8 kg | 23 | g/10 min | ASTM D1238 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 220°C/10.0 kg | 78 | g/10 min | ISO 1133 |
| OPTICAL |
|---|
| Light Transmission, 2.54 mm | 92 | % | ASTM D1003 |
| Haze, 2.54 mm | 1.3 | % | ASTM D1003 |
| Yellowness Index | 1 | - | ASTM D1925 |