CYCOLAC™	牌号	INP563	种类	ABS
CYCOLAC™	产品说明	Medium flow powder SAN for color concentrates and alloys. FDA compliant (part use must be at room temperature or below).

SABIC CYCOLAC™ ABS INP563 物性表

属性	典型值	UNITS	测试手段
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min	69	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	69	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Modulus, 5 mm/min	3860	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	93	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3770	MPa	ASTM D790
Hardness, Rockwell R	123	-	ASTM D785
Tensile Stress, yield, 50 mm/min	74	MPa	ISO 527
Tensile Stress, break, 50 mm/min	74	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	2	%	ISO 527
Tensile Strain, break, 50 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	3970	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	46	MPa	ISO 178
Flexural Modulus, 2 mm/min	3460	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	18	J/m	ASTM D256
Izod Impact, notched, -30°C	22	J/m	ASTM D256
Izod Impact, notched 80104 +23°C	2	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	2	kJ/m²	ISO 180/1A
Charpy Impact, notched, 23°C	1	kJ/m²	ISO 179/2C
THERMAL
HDT, 0.45 MPa, 3.2 mm	95	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	82	°C	ASTM D648
Vicat Softening Temp, Rate B/50	102	°C	ISO 306
Vicat Softening Temp, Rate B/120	104	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	85	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.08	-	ASTM D792
Melt Flow Rate, 230°C/3.8 kg	19.5	g/10 min	ASTM D1238
Density	1.08	g/cm³	ISO 1183
Melt Flow Rate, 220°C/10.0 kg	47	g/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm	92	%	ASTM D1003
Haze, 2.54 mm	1.5	%	ASTM D1003