| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 43 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 26 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2130 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 68 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 373 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 31 | J | ASTM D3763 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 98 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 82 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 8.82E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.64E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.05 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method |
| Melt Flow Rate, 230°C/3.8 kg | 3.7 | g/10 min | ASTM D1238 |
| Melt Viscosity, 240°C, 1000 sec-1 | 2450 | Poise | ASTM D3825 |
| Melt Flow Rate, 220°C/10.0 kg | 15 | g/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 1.52 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 80-95 | °C | |
| Drying Time | 2-4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 220-260 | °C | |
| Nozzle Temperature | 220-260 | °C | |
| Front - Zone 3 Temperature | 215-240 | °C | |
| Middle - Zone 2 Temperature | 205-225 | °C | |
| Rear - Zone 1 Temperature | 190-210 | °C | |
| Mold Temperature | 50-70 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 30-60 | rpm | |
| Shot to Cylinder Size | 50-70 | % | |
| Vent Depth | 0.038-0.051 | mm | |