| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 42.9 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2130 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 73 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2400 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 421 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 35 | J | ASTM D3763 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 94 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 82 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.92E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.1E-05 | 1/°C | ASTM E831 |
| PHYSICAL |
|---|
| Specific Gravity | 1.04 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Viscosity, 240°C, 100 sec-1 | 11600 | Poise | ASTM D3825 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 9 | cm³/10 min | ISO 1133 |
| Sheet Extrusion |
|---|
| Drying Temperature | 90-95 | °C | |
| Drying Time (Cumulative) | 4 | Hrs | |
| Maximum Moisture Content | 0 | % | |
| Melt Temperature | 200-220 | °C | |
| Barrel - Zone 1 Temperature | 170-190 | °C | |
| Barrel - Zone 2 Temperature | 180-200 | °C | |
| Barrel - Zone 3 Temperature | 175-205 | °C | |
| Barrel - Zone 4 Temperature | 180-210 | °C | |
| Adapter Temperature | 180-205 | °C | |
| Die Temperature | 180-215 | °C | |