| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 35 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 28 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 108 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 1680 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 57 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1900 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 464 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 320 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 39 | J | ASTM D3763 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 91 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 77 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.17E-04 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.03 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7-0.9 | % | SABIC method |
| Melt Viscosity, 240°C, 100 sec-1 | 15200 | Poise | ASTM D3825 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 4 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 1.52 | mm | UL 94 |
| Extrusion Blow Molding |
|---|
| Drying Temperature | 80-90 | °C | |
| Drying Time | 5-4 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02-0.04 | % | |
| Minimum Moisture Content | 0.04 | % | |
| Melt Temperature (Parison) | 210-225 | °C | |
| Barrel - Zone 1 Temperature | 190-220 | °C | |
| Barrel - Zone 2 Temperature | 190-220 | °C | |
| Barrel - Zone 3 Temperature | 190-220 | °C | |
| Barrel - Zone 4 Temperature | 190-220 | °C | |
| Adapter - Zone 5 Temperature | 195-220 | °C | |
| Head - Zone 6 - Top Temperature | 195-220 | °C | |
| Head - Zone 7 - Bottom Temperature | 195-220 | °C | |
| Screw Speed | 20-60 | rpm | |
| Extruder Feed Zone Temperature | 60-80 | °C | |
| Mold Temperature | 40-90 | °C | |
| Die Temperature | 195-220 | °C | |
| Sheet Extrusion |
|---|
| Drying Temperature | 90-95 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0 | % | |
| Melt Temperature | 210-240 | °C | |
| Barrel - Zone 1 Temperature | 195-210 | °C | |
| Barrel - Zone 2 Temperature | 200-220 | °C | |
| Barrel - Zone 3 Temperature | 205-230 | °C | |
| Barrel - Zone 4 Temperature | 210-235 | °C | |
| Adapter Temperature | 200-225 | °C | |
| Die Temperature | 210-240 | °C | |