| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 38 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 5 mm/min | 47 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 40 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 12 | % | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 85 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2240 | MPa | ASTM D638 |
| Tensile Stress, yield, 5 mm/min | 47 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 36 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 39 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 50 | % | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 12 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 74 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 80 | MPa | ISO 2039-1 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 380 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 115 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 19 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 +23°C | 28 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 11 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 22 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 85 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 8.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.3E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate A/120 | 120 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 103 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 84 | °C | ISO 75/Af |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 220°C/10.0 kgf | 10 | g/10 min | ASTM D1238 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 10 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| Injection Molding |
|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 245 - 275 | °C | |
| Front - Zone 3 Temperature | 250 - 280 | °C | |
| Middle - Zone 2 Temperature | 250 - 280 | °C | |
| Rear - Zone 1 Temperature | 230 - 260 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 40 - 80 | °C | |