| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield, 5 mm/min | 46 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 69 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 91 | MPa | ISO 2039-1 |
| IMPACT |
|---|
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 9.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 87 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-236566 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 90-100 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 250-280 | °C | |
| Nozzle Temperature | 245-275 | °C | |
| Front - Zone 3 Temperature | 250-280 | °C | |
| Middle - Zone 2 Temperature | 250-280 | °C | |
| Rear - Zone 1 Temperature | 230-260 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Mold Temperature | 40-80 | °C | |