| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 42 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 35 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 11 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2410 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 73 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2720 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 267 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 41 | J | ASTM D3763 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 90 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 83 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 72 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.92E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.92E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.17 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 230°C/3.8 kg | 6.8 | g/10 min | ASTM D1238 |
| Melt Viscosity, 200°C, 1000 sec-1 | 3100 | Poise | ASTM D3825 |
| Melt Flow Rate, 220°C/5.0 kg | 9 | g/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 37 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E207780-228348 | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 2.31 | mm | UL 94 |
| UL Recognized, 94-5VB Flame Class Rating | 2.48 | mm | UL 94 |