| INFINO® | 牌号 | TL-2058 | 种类 | PCT/GF |
| 特性 | 一般 | |||
| INFINO® | 牌号 | TL-2058 | 种类 | PCT/GF |
| 特性 | 一般 | |||
| 项目 | 测试方法 | 条件 | 单位 | 代表值 |
|---|
| 物理性质 | ||||
|---|---|---|---|---|
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.71 |
| 熔融指数 | ASTM D1238 | 300℃, 1.2kg | g/10min | 25 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.4-0.7 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.4-0.7 |
| ASH content | ASTM D5630 | - | % | 46.0 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 530 |
| 伸长率(at break) | ASTM D638 | 5mm/min | % | 2.0 |
| 拉伸模量- | ASTM D638 | 5mm/min | kgf/cm2 | - |
| 断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 530 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 530 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 64,000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 1.5 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 1.9 |
| Izod冲击强度(unnotched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 10 |
| Izod冲击强度(unnotched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 11 |
| 硬度 | ASTM D785 | R-Scale | - | - |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 230 |
| 光学性质 | ||||
|---|---|---|---|---|
| 初期反射率 | E 1331 | % | 94.5↑ | |
| 项目 | 单位 | 代表值 | ||
|---|---|---|---|---|
| 模具温度(Standard Molding) | 固定轴 | °C | 110 ~ 130 | |
| 移动轴 | ||||
| Hot Runner 温度 | Manifold | °C | 0 | |
| Valve nozzle | 0 | |||
| Nozzle温度 | °C | 305~310 | ||
| Cylinder温度 | 前端 | °C | 305 ~ 310 | |
| 中部 | 300 ~ 300 | |||
| 下部 | 290 ~ 300 | |||
| 注塑压力 | kgf/cm2 | 80~130 | ||
| 干燥条件 | 干燥方式 | 干燥温度 | °C | 80~100 |
| 干燥时间 | hr | 4 | ||
| 热风方式 | 干燥温度 | °C | 100 | |
| 干燥时间 | hr | 4 | ||
| 干燥后合适水分量 | % | 0.06 | ||
| 计量速度 | rpm | 180 ~ 250 | ||
| 背压 | kgf/cm2 | 80 ~ 130 | ||