韩国乐天 Starex ABS SV-0165 U 物性表
物理性质
| 物理性质 |
| 比重 |
ASTM D792 |
Natural 或代表 color |
- |
1.04 |
| 熔融指数 |
ASTM D1238 |
220℃, 10kg |
g/10min |
8.2 |
| 成型收缩率(MD) |
ASTM D955 |
Flow at 3.2mm(MD) |
% |
0.5~0.6 |
| 成型收缩率(TD) |
ASTM D955 |
X-Flow at 3.2mm(TD) |
% |
0.5~0.6 |
机械性质
| 机械性质 |
| 拉伸强度(at yield) |
ASTM D638 |
5mm/min |
kgf/cm2 |
400 |
| 伸长率(at break) |
ASTM D638 |
5mm/min |
% |
20 |
| 拉伸模量24000 |
ASTM D638 |
5mm/min |
kgf/cm2 |
24000 |
| 断裂强度(at break) |
ASTM D638 |
5mm/min |
kgf/cm2 |
370 |
| 弯曲强度 |
ASTM D790 |
2.8mm/min |
kgf/cm2 |
770 |
| 弯曲模量 |
ASTM D790 |
2.8mm/min |
kgf/cm2 |
26000 |
| Izod冲击强度(notched) |
ASTM D256 |
1/4 inch at 23°C |
kgf·cm/cm |
22 |
| Izod冲击强度(notched) |
ASTM D256 |
1/8 inch at 23°C |
kgf·cm/cm |
25 |
| 硬度 |
ASTM D785 |
R-Scale |
- |
109 |
热学特性
| 热学特性 |
| 热变形温度 |
ASTM D648 |
18.56kgf/cm2, 6.4mm |
°C |
88 |
| 热变形温度 |
ASTM D648 |
4.6kgf/cm2, 6.4mm |
°C |
98 |
| 维卡软化温度 |
ISO 306 |
B/50 |
°C |
100 |
阻燃
| 阻燃 |
| 阻燃度 |
UL94 |
HB |
mm |
1.5, 3.0 |
SV-0165 U 注塑工艺
加工条件表
| 项目 |
单位 |
代表值 |
| 模具温度(Standard Molding) |
固定轴 |
°C |
80 ~ 60 |
| 移动轴 |
|
| Hot Runner 温度 |
Manifold |
°C |
230 |
| Valve nozzle |
220 |
| Nozzle温度 |
|
°C |
230 |
| Cylinder温度 |
前端 |
°C |
230 ~ 220 |
| 中部 |
220 ~ 210 |
| 下部 |
210 ~ 200 |
| 注塑压力 |
|
kgf/cm2 |
120 |
| 干燥条件 |
干燥方式 |
干燥温度 |
°C |
80 |
| 干燥时间 |
hr |
2 |
| 热风方式 |
干燥温度 |
°C |
80 |
| 干燥时间 |
hr |
4 |
| 干燥后合适水分量 |
|
% |
0.01 |
| 计量速度 |
|
rpm |
100 ~ 30 |
| 背压 |
|
kgf/cm2 |
120 ~ 40 |