| Thermal properties |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 2.9 mm | Class | HB (CL) |
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-2 (CL) |
| Burning rate (US-FMVSS) | ISO 3795 | >=1.0 mm | mm/min | passed |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Flash ignition temperature | ASTM D1929 | | °C | 480 |
| Glass transition temperature | ISO 11357-1,-2 | 10 °C/min | °C | 145 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.0 mm | °C | 850 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 875 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 930 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 0.75 mm | °C | 875 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 875 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 900 |
| Oxygen index | ISO 4589-2 | Method A | % | 28 |
| Relative temperature index (Electric strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Relative temperature index (Tensile impact strength) [UL recognition] | UL 746B | 1.5 mm | °C | 115 |
| Relative temperature index (Tensile strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Resistance to heat (ball pressure test) | IEC 60695-10-2 | | °C | 136 |
| Self ignition temperature | ASTM D1929 | | °C | 550 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 138 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 125 |
| Thermal conductivity, through-plane | ISO 8302 | 23 °C; 50 % r. h. | W/(m*K) | 0.2 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 146 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 145 |
| Mechanical properties (23 °C/50 % r. h.) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Ball indentation hardness | ISO 2039-1 | | N/mm² | 115 |
| Charpy impact strength | ISO 179/1eU | -60 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C/ 3 mm | kJ/m² | 12C |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C/ 3 mm | kJ/m² | 60P(C) |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2350 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 7.1 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 97 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 73 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 55P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 12C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 60 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 55 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 5900 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4900 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 125 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2350 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Material specific properties |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Haze for transparent materials | ISO 14782 | 3 mm | % | < 0.5 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 1 mm | % | 90 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 2 mm | % | 90 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 4 mm | % | > 89 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 3 mm | % | > 89 |
| Refractive index | ISO 489 | Procedure A | | 1.584 |
| Rheological properties |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 34 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm/ 500 bar | % | 0.7 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm/ 500 bar | % | 0.65 |
| Electrical properties (23 °C/50 % r. h.) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 250 |
| Comparative tracking index CTI M | IEC 60112 | Solution B | Rating | 125M |
| Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 95 |
| Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 5 |
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 34 |
| Relative permittivity | IEC 60250 | 1 MHz | | 3.0 |
| Relative permittivity | IEC 60250 | 100 Hz | | 3.1 |
| Surface resistivity | IEC 60093 | | Ohm | 1E16 |
| Volume resistivity | IEC 60093 | | Ohm*m | 1E14 |
| Processing conditions for test specimens |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Injection molding - Injection velocity | ISO 294 | | mm/s | 200 |
| Injection molding - Melt temperature | ISO 294 | | °C | 280 |
| Injection molding - Mold temperature | ISO 294 | | °C | 80 |
| Other properties (23 °C) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Bulk density | ISO 60 | Pellets | kg/m³ | 660 |
| Density | ISO 1183-1 | | kg/m³ | 1190 |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.12 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.3 |