| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 78 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2310 | MPa | ASTM D790 |
| Flexural Stress, yield, 2 mm/min | 97 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 910 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 128 | J/m | ASTM D256 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 6.06E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.16E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| PHYSICAL |
|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Mold Shrinkage, flow | 0.77 | % | SABIC method |
| Mold Shrinkage, xflow | 0.77 | % | SABIC method |
| Water Absorption, (23°C/saturated) | 0.14 | % | ISO 62-1 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 8 | cm³/10 min | ISO 1133 |
| OPTICAL |
|---|
| Light Transmission, 2.54 mm | 87 | % | ASTM D1003 |
| Haze, 2.54 mm | 0.4 | % | ASTM D1003 |
| ELECTRICAL |
|---|
| Dielectric Constant, 1.1 GHz | 2.8 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.0063 | - | SABIC method |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280-310 | °C | |
| Nozzle Temperature | 270-290 | °C | |
| Front - Zone 3 Temperature | 280-310 | °C | |
| Middle - Zone 2 Temperature | 270-290 | °C | |
| Rear - Zone 1 Temperature | 260-280 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Mold Temperature | 80-110 | °C | |