| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| PHYSICAL |
|---|
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
| Profile Extrusion |
|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 2-3 | Hrs | |
| Melt Temperature | 220-250 | °C | |
| Barrel - Zone 1 Temperature | 240-280 | °C | |
| Barrel - Zone 2 Temperature | 240-280 | °C | |
| Barrel - Zone 3 Temperature | 220-240 | °C | |
| Barrel - Zone 4 Temperature | 220-240 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Adapter Temperature | 220-240 | °C | |
| Die Temperature | 245-290 | °C | |
| Calibrator Temperature | 60-100 | °C | |