| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 81 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2030 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 640 | J/m | ASTM D256 |
| Izod Impact, notched, -20°C | 587 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 213 | J/m | ASTM D256 |
| Izod Impact, notched, 23°C, 6.4mm | 213 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 56 | J | ASTM D3763 |
| THERMAL |
|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 118 | °C | ASTM D648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 126 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 123 | °C | ASTM D648 |
| CTE, -40°C to 95°C, flow | 6.48E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.16 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 20 | g/10 min | ASTM D1238 |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 1.47 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3-4 | Hrs | |
| Drying Time (Cumulative) | 10 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 275-300 | °C | |
| Nozzle Temperature | 270-295 | °C | |
| Front - Zone 3 Temperature | 275-300 | °C | |
| Middle - Zone 2 Temperature | 265-290 | °C | |
| Rear - Zone 1 Temperature | 255-275 | °C | |
| Mold Temperature | 70-95 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 40-70 | rpm | |
| Shot to Cylinder Size | 40-60 | % | |
| Vent Depth | 0.025-0.076 | mm | |