韩国乐天 INFINO PC UH-1064 物性表
物理性质
| 物理性质 |
| 比重 |
ASTM D792 |
Natural 或代表 color |
- |
1.19 |
| 熔融指数 |
ASTM D1238 |
300℃, 1.2kg |
g/10min |
16 |
| 成型收缩率(MD) |
ASTM D955 |
Flow at 3.2mm(MD) |
% |
0.4-0.7 |
| 成型收缩率(TD) |
ASTM D955 |
X-Flow at 3.2mm(TD) |
% |
0.4-0.7 |
机械性质
| 机械性质 |
| 拉伸强度(at yield) |
ASTM D638 |
50mm/min |
kgf/cm2 |
600 |
| 伸长率(at break) |
ASTM D638 |
50mm/min |
% |
90 |
| 拉伸模量20000 |
ASTM D638 |
50mm/min |
kgf/cm2 |
20000 |
| 断裂强度(at break) |
ASTM D638 |
50mm/min |
kgf/cm2 |
550 |
| 弯曲强度 |
ASTM D790 |
2.8mm/min |
kgf/cm2 |
850 |
| 弯曲模量 |
ASTM D790 |
2.8mm/min |
kgf/cm2 |
21000 |
| Izod冲击强度(notched) |
ASTM D256 |
1/4 inch at 23°C |
kgf·cm/cm |
45 |
| Izod冲击强度(notched) |
ASTM D256 |
1/8 inch at 23°C |
kgf·cm/cm |
75 |
| 硬度 |
ASTM D785 |
R-Scale |
- |
118 |
热学特性
| 热学特性 |
| 热变形温度 |
ASTM D648 |
18.56kgf/cm2, 6.4mm |
°C |
123 |
| 热变形温度 |
ASTM D648 |
4.6kgf/cm2, 6.4mm |
°C |
- |
| 维卡软化温度 |
ISO 306 |
B/50 |
°C |
139 |
阻燃
| 阻燃 |
| 阻燃度 |
UL94 |
V-0 |
mm |
1.5, 3.0 |
| Glow-Wire Flammability Index |
IEC 60695-2-12 |
960 |
°C |
1.5, 3.0 |
| Glow-Wire Ignition Index |
IEC 60695-2-13 |
825 |
°C |
1.5, 3.0 |
电气性能
| 电气性能 |
| Hot Wire Ignition |
UL746A |
3 |
PLC |
1.5 |
| High Current Arc Ignition |
UL746A |
3 |
PLC |
1.5 |
| Comparative Tracking Index |
IEC 60112 |
- |
PLC |
3 |
UH-1064 注塑工艺
加工条件表
| 项目 |
单位 |
代表值 |
| 模具温度(Standard Molding) |
固定轴 |
°C |
70 ~ 100 |
| 移动轴 |
|
| Hot Runner 温度 |
Manifold |
°C |
290-310 |
| Valve nozzle |
290-310 |
| Nozzle温度 |
|
°C |
290-310 |
| Cylinder温度 |
前端 |
°C |
280 ~ 290 |
| 中部 |
260 ~ 270 |
| 下部 |
240 ~ 250 |
| 注塑压力 |
|
kgf/cm2 |
500-2500 |
| 干燥条件 |
干燥方式 |
干燥温度 |
°C |
100 |
| 干燥时间 |
hr |
2-4 |
| 热风方式 |
干燥温度 |
°C |
120 |
| 干燥时间 |
hr |
2-6 |
| 干燥后合适水分量 |
|
% |
<0.05 |
| 计量速度 |
|
rpm |
50 ~ 150 |
| 背压 |
|
kgf/cm2 |
5 ~ 20 |