| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 143 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 97 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D790 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 801 | J/m | ASTM D256 |
| THERMAL |
|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 123 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 133 | °C | ASTM D648 |
| PHYSICAL |
|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.15 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 18 | g/10 min | ASTM D1238 |
| Injection Molding |
|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Melt Temperature | 280 - 305 | °C | |
| Mold Temperature | 70 - 95 | °C | |