| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 42 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 27 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2370 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 71 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2290 | MPa | ASTM D790 |
| Hardness, Rockwell R | 104 | - | ASTM D785 |
| Tensile Stress, yield, 50 mm/min | 46 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 35 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2.6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 18 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 69 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2170 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 300 | J/m | ASTM D256 |
| Izod Impact, notched, 23°C, 6.4mm | 240 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 9 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 25 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 99 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 93 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 104 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.04 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method |
| Melt Flow Rate, 230°C/3.8 kg | 3.5 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 260°C/5.0 kgf | 18 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 220°C/10.0 kg | 10 | g/10 min | ISO 1133 |
| FLAME CHARACTERISTICS |
|---|
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| Injection Molding |
|---|
| Drying Temperature | 90-95 | °C | |
| Drying Time | 2-4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 230-275 | °C | |
| Nozzle Temperature | 230-275 | °C | |
| Front - Zone 3 Temperature | 230-255 | °C | |
| Middle - Zone 2 Temperature | 210-225 | °C | |
| Rear - Zone 1 Temperature | 195-210 | °C | |
| Mold Temperature | 50-80 | °C | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 30-60 | rpm | |
| Shot to Cylinder Size | 50-70 | % | |
| Vent Depth | 0.038-0.051 | mm | |